以氯化大豆油和大豆油丙烯酸酯为多元醇,与异氟尔酮二异氰酸酯、2,2-二羟甲基丙酸反应合成大豆油基水性聚氨酯(SWPU)。以SWPU的双键为反应位点,以甲基丙烯酸甲酯和丙烯酸丁酯为单体,采用无皂乳液聚合接枝共聚合成了一系列聚丙烯酸酯接枝大豆油基水性聚氨酯(SPUA)。红外光谱、激光粒度仪等测试结果表明,成功制备了接枝共聚物SPUA。与SWPU胶膜相比,SPUA胶膜的吸水率显著降低,硬度明显提高,机械性能和热稳定性也得到提升。
Soybean oil-based waterborne polyurethane (SWPU) was synthesized by the reaction of chlorinated soybean oil,soybean oil acrylate,isophorone diisocyanate and 2,2-dimethylolpropionic acid.Soybean oil-based waterborne polyurethane grafted polyacrylate (SPUA) emulsion was prepared by soap-free emulsion polymerization using double bond in SWPU as reaction sites and methyl methacrylate and butyl acrylate as monomers.The results of Fourier transform infrared spectroscopy and laser particle size analyzer showed that the grafted copolymer was successfully prepared.In comparison with the SWPU film,the water absorption of SPUA film was significantly reduced,the hardness was obviously improved,and the mechanical properties and thermal stability were also improved.
[1] 严加安,胡兆平,陈剑秋,等.可降解功能化聚氨酯材料的研究进展[J].化工新型材料,2018,46(5):218-221.
[2] 李秀峥,李澜鹏,曹长海,等.植物油多元醇的研究及商业化应用进展[J].聚氨酯工业,2018,33(02):1-4.
[3] Patil C K,Rajput S D,Marathe R J,et al.Synthesis of bio-based polyurethane coatings from vegetable oil and dicarboxylic acids[J].Progress in Organic Coatings,2017,106:87-95.
[4] Moghadam P N,Yarmohamadi M,Hasanzadeh R,et al.Preparation of polyurethane wood adhesives by polyols formulated with polyester polyols based on castor oil[J].International Journal of Adhesion and Adhesives,2016,68:273-282.
[5] Karimi M B,Khanbabaei G,Sadeghi G M M.Vegetable oil-based polyurethane membrane for gas separation[J].Journal of Membrane Science,2017,527:198-206.
[6] Yadav S,Zafar F,Hasnat A,et al.Poly (urethane fatty amide) resin from linseed oil—a renewable resource[J].Progress in Organic Coatings,2009,64(1):27-32.
[7] Kong X,Liu G,Qi H,et al.Preparation and characterization of high-solid polyurethane coating systems based on vegetable oil derived polyols[J].Progress in Organic Coatings,2013,76(9):1151-1160.
[8] Liu H,Lu W,Liu S.Development of acrylated soybean oil-based UV-curable coatings with high impact strength from low viscosity oligomer[J].Journal of Applied Polymer Science,2017,134:45698.
[9] Zhao Z,Jing Z,Qiu F,et al.Preparation,thermal property and morphology analysis of waterborne polyurethane-acrylate[J].AIP Conference Proceedings,2017,1794.
[10] Lu Y,Larock R C.New hybrid latexes from a soybean oil-based waterborne polyurethane and acrylics via emulsion polymerization[J].Biomacromolecules,2007,8(10):3108-3114.
[11] 付长清,黄伟,卢宗祥,等.无皂核壳蓖麻油基聚氨酯/聚氟化丙烯酸酯杂化乳液[J].电镀与涂饰,2013,32(05):59-62.
[12] Jiao Z,Wang X,Yang Q,et al.Modification and characterization of urethane acrylate oligomers used for UV-curable coatings[J].Polymer Bulletin,2017,74(7):2497-2511.
[13] Yi T,Ma G,Hou C,et al.Polyurethane-acrylic hybrid emulsions with high acrylic/polyurethaneratios:synthesis,characterization,and properties[J].Journal of Applied Polymer Science,2016,133,44488.
[14] Wang C,Chen X,Chen J,et al.Synthesis and characterization of novel polyurethane acrylates based on soy polyols[J].Journal of Applied Polymer Science,2011,122(4):2449-2455.
[15] Lu Y,Xia Y,Larock R C.Surfactant-free core-shell hybrid latexes from soybean oil-based waterborne polyurethanes and poly(styrene-butyl acrylate)[J].Progress in Organic Coatings,2011,71(4):336-342.
[16] Jin L,Liu Z,Xu Q,et al.Preparation of soap-free cationic emulsion using polymerizable surfactant[J].Journal of Applied Polymer Science,2006,99(3):1111-1116.
[17] Xin H,Shen Y,Li X.Novel cationic polyurethane-fluorinated acrylic hybrid latexes:synthesis,characterization and properties[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2011,384(1):205-211.
[18] 王学川,宗奕珊,强涛涛.无皂蓖麻油基聚氨酯-丙烯酸酯复合乳液的制备与性能研究[J].功能材料,2014(15):15070-15074.
[19] Zhang H T,Guan R,Yin Z H,et al.Soap-free seeded emulsion copolymerization of MMA onto PU-A and their properties[J].Journal of Applied Polymer Science,2001,82:941-947.
[20] 王雪琴,夏萍,蔡彦.无皂乳液聚合制备PUA乳液的稳定性研究[J].粘接,2010,10:44-47.
基金资助
河北省重点基础研究计划项目(18961211D)
PDF